The structure formation of rapidly solidified foil of the eutectic alloy Sn – 8,8 wt. % Zn

D.A. Zernitsa¹, V.G. Shepelevich²

¹ Mozyr State Pedagogical University named after I.P. Shamiakin
² Belarusian State University

DOI: 10.26456/pcascnn/2020.12.601

Original article

Abstract: The results are presenred of a study of the microstructure of rapidly solidified foil of the eutectic alloy Sn – 8,8 wt.% Zn A and B surfaces, microstructure parameters are determined. The texture of the precipitates of tin and zinc solid solutions in the foil was studied, and the pole densities of the diffraction lines of these phases are presented. The effect is studied of ultrafast cooling on the distribution of misorientation angles of neighboring and randomly selected grains for surface foil layers in contact with surfaces A and B.

Keywords: rapidly solidification, Sn - Zn alloy, eutectic, microstructure, texture, spinodal decomposition, disorientation, twinning

• Denis A. Zernitsa – postgraduate student of the Department of Physics and Mathematics, Faculty of Physics and Engineering, Mozyr State Pedagogical University named after I.P. Shamiakin
• Vasilii G. Shepelevich – Dr. Sc., Professor of the Department of Solid State Physics, Faculty of Physics, Belarusian State University

Reference:

Zernitsa, D.A. The structure formation of rapidly solidified foil of the eutectic alloy Sn – 8,8 wt. % Zn / D.A. Zernitsa, V.G. Shepelevich // Physical and chemical aspects of the study of clusters, nanostructures and nanomaterials. — 2020. — I. 12. — P. 601-608. DOI: 10.26456/pcascnn/2020.12.601. (In Russian).

Full article (in Russian): download PDF file

⇐ Prevoius journal article | Content | Next journal article ⇒