ELECTROCHEMICAL DEPOSITION OF CALCIUM PHOSPHATE COATINGS ONTO TITANIUM AND CARBON SUBSTRATES
V.K. Krut'ko, A.I. Kulak, O.N. Musskaya, L.A. Lesnikovich, S.A. Ulasevich
DOI: 10.26456/pcascnn/2014.6.214
Original article
Abstract: The calcium phosphate coatings on titanium and carbon (fabric, felt) substrates have been
obtained using electrochemical deposition in CaCl2 − NH4H2PO4 water electrolyte at рН 3,2 − 3,6
and room temperature. In accordance with XRD data it was determined that the calcium phosphate
coatings consist of brushite CaHPO4 ⋅ 2H2O, α -tricalcium phosphate Ca3(PO4)2 and additional
amount of octacalcium phosphate phase Ca8H2(PO4)6 ⋅ 5H2O on carbon substrates.
Keywords: calcium phosphates, biocompatible coatings, electrodeposition
- V.K. Krut'ko
- A.I. Kulak
- O.N. Musskaya
- L.A. Lesnikovich
- S.A. Ulasevich
Reference:
Krut'ko V.K., Kulak A.I., Musskaya O.N., Lesnikovich L.A., Ulasevich S.A. Elektrokhimicheskoe osazhdenie kaltsijfosfatnykh pokrytij na titanovoj i uglerodnykh podlozhkakh [ELECTROCHEMICAL DEPOSITION OF CALCIUM PHOSPHATE COATINGS ONTO TITANIUM AND CARBON SUBSTRATES], Fiziko-khimicheskie aspekty izucheniya klasterov, nanostruktur i nanomaterialov [Physical and chemical aspects of the study of clusters, nanostructures and nanomaterials], 2014, issue 6, pp. 214-219. DOI: 10.26456/pcascnn/2014.6.214. ⎘
Full article (in Russian): download PDF file
⇐ Prevoius journal article | Content | Next journal article ⇒